Home page / Catalogue / Products of «BRP» / Molded goods / Stopper refractory products for steel teeming from ladle
Stopper refractory products
Stopper refractory products are used for steel teeming from ladle
Technical characteristics
|
Norm for mark |
|||||||
---|---|---|---|---|---|---|---|---|
|
Stopper tubes |
|||||||
SHST-32 |
SHST-35 |
MLST-63 |
MKST-73 |
MKSTT-73 |
MKBST-75 |
|||
GOST R 53066-2008 |
||||||||
Mass fraction, %: Al2O3, no less Fe2O3, no more |
32 - |
35 - |
63 1,3 |
73 1,1 |
73 1,5 |
75 2,2 |
||
Refractory property, °C, no low than |
1690 |
1710 |
- |
- |
- |
- |
||
Open porosity, %, in the limit of: - semidry pressing - soft mud shaping |
15-26 19-26 |
16-21 - |
16-20 - |
no more - |
17-22 - |
|||
Residual changes in the sizes during heating, %, no more than, at the temperature: 1350 °C 1400 °C |
0,3 - |
- 0,1 |
- 0,1 |
- 0,3 |
- 0,1 |
|||
Thermal resistance, thermal cycling , no less |
1 |
2 |
2 |
3 |
2 |
|||
|
Norm for mark |
|||||||
|
Stopper pocket brick |
|||||||
SHSG-32 |
MLSG-62 |
|||||||
GOST R 53066-2008 |
||||||||
Mass fraction, %: |
|
|||||||
Al2O3 no less |
32 |
over |
||||||
Fe2O3, no more |
- |
1,5 |
||||||
Refractory property, °C, no low |
1690 |
- |
||||||
Open porosity, %, no more |
23 |
24 |
||||||
Compressive resistance, N/mm2, no less |
15 |
25 |
||||||
Onset temperature of softening, °C, no low |
- |
1450 |
||||||
Residual change in dimensions at the temperature 1500°C, no more |
- |
0,4 |
|
Norm for mark |
||||
---|---|---|---|---|---|
|
Stopper head |
||||
SHSP-32 |
SHSP-34 |
||||
GOST R 53066-2008 |
|||||
Mass fraction, %: Al2O3, no less |
32 |
34 |
|||
Refractory property, °C, no low |
1690 |
1710 |
|||
Open porosity, %, in the limit of: - semidry pressing - soft mud shaping |
15-20 18-23 |
15-20 18-22 |
|||
Onset temperature of softening, °C, no low - semidry pressing - soft mud shaping |
1320 1350 |
||||
Thermal resistance, thermal cycling , no less |
1 |
3 |
|||
|
Norm for mark |
||||
|
Stopper nozzle |
||||
SHSS-32 |
SHSS -34 |
MLSS-62 |
|||
GOST R 53066-2008 |
|||||
Mass fraction, %: Al2O3, no less Fe2O3, no more |
32 - |
34 - |
over 62 1,5 |
||
Refractory property, °C, no low |
1690 |
1710 |
- |
||
Open porosity, %, no more |
22 |
20 |
24 |
||
Onset temperature of softening, °C, no low |
1350 |
- |